ASTM A269 Bright Annealed Stainless Steel Seamless Tubing
SSBA57
Price: From $9000-12000USD/TON
Material: 321,321H, 1.4541;
Get QuoteASTM A269 Chemical Composition :
Elements | 304L(wt%) S30403 | 304(wt%) S30400 | 316L (wt%) S31603 | 316 (wt%) S31600 |
(C) Carbon, max | 0.035 | 0.08 | 0.035 | 0.08 |
(Mn) Manganese, max | 2 | 2 | 2 | 2 |
(P) Phosphorus, max | 0.045 | 0.045 | 0.045 | 0.045 |
(S) Sulfur, max | 0.03 | 0.03 | 0.03 | 0.03 |
(Si) Silicon, max | 1 | 1 | 1 | 1 |
(Ni) Nickel | 8.0 - 12.0 | 8.0 - 11.0 | 10.0 - 14.0 | 10.0 - 14.0 |
(Cr) Chromium | 18.0 - 20.0 | 18.0 - 20.0 | 16.0 - 18.0 | 16.0 - 18.0 |
(Mo) Molybdenum | N/A | N/A | 2.0 - 3.0 | 2.0 - 3.0 |
(Fe) Iron | Bal. | Bal. | Bal. | Bal. |
(Cu) Copper | N/A | N/A | N/A | N/A |
(N) Nitrogen | N/A | N/A | N/A | N/A |
Advantages
a) Superior surface finish
b) Better mechanical property
c) More precise dimension
d) Perfect inspection method and inspection equipment
Price Item FOB , CFR , CIF or as negotiation
Payment TT, LC or as negotiation
Delivery Time 30 working days after received your deposit ( Normally according to the order quantity )
Package Iron case ; woven bag or as per customer’s requirement
Quality Requirement Mill Test Certificate will be supplied with shipment , Third Part Inspection is acceptable
Test NTD ( Ultrasonic test , Eddy Current test )
Mechanical Test ( Tension Test , Flaring Test , Flattening Test , Hardness Test , Hydraulic test )
Metal Test ( Metallographic Analysis , Impact Test - High / low temperature )
Chemical Analysis ( Photoelectric Emission Spectroscopic )
Main Market Europe , Middle East , Southeast Asia , South America etc
EN10216-5 Standard Chemical Composition :
Steel Grade | C | Si | Mn | P | S | N | Cr | Cu | Mo | Nb | Ni | Ti | Others | |
max | max | max | ||||||||||||
Steel Name | Steel Number | |||||||||||||
X2CrNi19-11 | 1.4306 | 0.03 | ≤1 | ≤2 | 0.04 | 0.015 | ≤0.11 | 18.00 - 20.00 | - | - | - | 8.00 - 10.00 | - | - |
X5CrNi18-10 | 1.4301 | 0.07 | ≤1 | ≤2 | 0.04 | 0.015 | ≤0.11 | 17.00 - 19.50 | - | - | - | 8.00 - 10.50 | - | - |
X6CrNiTi18-10 | 1.4541 | 0.08 | ≤1 | ≤2 | 0.04 | 0.015 | ≤0.11 | 17.00 - 19.00 | - | - | - | 9.00 - 12.00 | 5xC to 0.70 | - |
X6CrNiNb18-10 | 1.4550 | 0.08 | ≤1 | ≤2 | 0.04 | 0.015 | - | 17.00 - 19.00 | - | - | 10xC to 1.00 | 9.00 - 12.00 | - | - |
X2CrNiMo17-12-2 | 1.4404 | 0.03 | ≤1 | ≤2 | 0.04 | 0.015 | ≤0.11 | 16.50 - 18.50 | - | 2.00 - 2.50 | - | 10.00 - 13.00 | - | - |
X5CrNiMo17-12-2 | 1.4401 | 0.07 | ≤1 | ≤2 | 0.04 | 0.015 | ≤0.11 | 16.50 - 18.50 | - | 2.00 - 2.50 | - | 10.00 - 13.00 | - | - |
X6CrNiMoTi17-12-2 | 1.4571 | 0.08 | ≤1 | ≤2 | 0.04 | 0.015 | - | 16.50 - 18.50 | - | 2.00 - 2.50 | - | 10.50 - 13.50 | 5xC to 0.70 | - |
Stanard Wire Gauge ( Fomerly Imperial Wire Gauge ) SWG | |||||
SWG | Wall Thickness | SWG | Wall Thickness | ||
0 | 0.324 | 8.23 | 21 | 0.032 | 0.81 |
1 | 0.3 | 7.62 | 22 | 0.028 | 0.71 |
2 | 0.276 | 7.01 | 23 | 0.024 | 0.61 |
3 | 0.252 | 6.4 | 24 | 0.022 | 0.56 |
4 | 0.232 | 5.89 | 25 | 0.02 | 0.51 |
5 | 0.212 | 5.38 | 26 | 0.018 | 0.46 |
6 | 0.192 | 4.88 | 27 | 0.0164 | 0.42 |
7 | 0.176 | 4.47 | 28 | 0.0148 | 0.38 |
8 | 0.16 | 4.06 | 29 | 0.0136 | 0.35 |
9 | 0.144 | 3.66 | 30 | 0.0124 | 0.31 |
10 | 0.128 | 3.25 | 31 | 0.0116 | 0.29 |
11 | 0.116 | 2.95 | 32 | 0.0108 | 0.27 |
12 | 0.104 | 2.64 | 33 | 0.01 | 0.25 |
13 | 0.092 | 2.34 | 34 | 0.0092 | 0.23 |
14 | 0.08 | 2.03 | 35 | 0.0084 | 0.21 |
15 | 0.072 | 1.83 | 36 | 0.0076 | 0.19 |
16 | 0.064 | 1.63 | 37 | 0.0068 | 0.17 |
17 | 0.056 | 1.42 | 38 | 0.006 | 0.15 |
18 | 0.048 | 1.22 | 39 | 0.0052 | 0.13 |
19 | 0.04 | 1.02 | 40 | 0.0048 | 0.12 |
20 | 0.036 | 0.91 |